鐵藝護欄的焊接點是確保整體結構穩定的關鍵，其牢固性直接關系到護欄的安全性能與使用壽命。要保證焊接點牢固，需從焊接前的準備、焊接過程中的操作以及焊接后的處理等多個環節嚴格把控。

　　The welding points of wrought iron guardrails are the key to ensuring overall structural stability, and their firmness directly affects the safety performance and service life of the guardrails. To ensure the firmness of the welding point, it is necessary to strictly control multiple aspects such as preparation before welding, operation during the welding process, and treatment after welding.

　　焊接前的基礎準備不可或缺。首先要對焊接部位進行徹底清理，去除表面的鐵銹、油污、氧化皮等雜質，可采用砂紙打磨或鋼絲刷清理的方式，確保金屬母材露出光澤，避免雜質影響焊縫的結合強度。其次，需檢查焊條或焊絲的規格與鐵藝護欄材質是否匹配，例如低碳鋼材質的護欄應選用相應型號的低碳鋼焊條，確保焊接時能形成良好的熔合區。同時，要調整好焊接設備的參數，如電流大小、電壓等級等，根據護欄管材的厚度和焊接位置進行適配設置，避免因參數不當導致焊不透或燒穿等問題。

　　Basic preparation before welding is indispensable. Firstly, the welding area should be thoroughly cleaned to remove impurities such as rust, oil stains, and oxide scales on the surface. Sandpaper polishing or wire brush cleaning can be used to ensure that the metal base material is exposed to gloss and avoid impurities affecting the bonding strength of the weld. Secondly, it is necessary to check whether the specifications of the welding rod or wire match the material of the iron guardrail. For example, for guardrails made of low-carbon steel, the corresponding model of low-carbon steel welding rod should be selected to ensure that a good fusion zone can be formed during welding. At the same time, it is necessary to adjust the parameters of the welding equipment, such as current size, voltage level, etc., according to the thickness and welding position of the guardrail pipe, to avoid problems such as incomplete welding or burning through caused by improper parameters.

　　焊接過程中的操作規范是保障牢固性的核心。焊接時應保證焊條與焊接點之間保持穩定的角度和距離，一般焊條與工件的夾角以 45 度左右為宜，運條速度需均勻，確保焊縫金屬能充分填滿熔池。對于較厚的管材或重要節點，應采用多層多道焊接方式，每層焊縫需清理干凈焊渣后再進行下一層焊接，避免夾渣、氣孔等缺陷。焊接過程中要注意觀察熔池狀態，確保母材與填充金屬完全熔合，形成連續、致密的焊縫，避免出現未焊透、裂紋等影響強度的問題。此外，在拐角、交叉等應力集中的部位，應適當增加焊接長度和焊腳尺寸，增強焊接點的承載能力。

　　The operational standards during the welding process are the core to ensure firmness. During welding, it is necessary to ensure a stable angle and distance between the welding rod and the welding point. Generally, the angle between the welding rod and the workpiece should be around 45 degrees. The speed of the welding rod should be uniform to ensure that the weld metal can fully fill the molten pool. For thicker pipes or important nodes, multi-layer and multi pass welding should be used, and each layer of weld seam should be cleaned of welding slag before proceeding to the next layer of welding to avoid defects such as slag inclusion and porosity. During the welding process, attention should be paid to observing the state of the molten pool to ensure complete fusion between the base metal and the filler metal, forming a continuous and dense weld seam, and avoiding problems such as incomplete penetration and cracks that affect strength. In addition, in stress concentration areas such as corners and intersections, the welding length and weld leg size should be appropriately increased to enhance the load-bearing capacity of the welding point.

　　焊接后的處理同樣影響焊接點的牢固性與耐久性。焊接完成后，需及時清理焊縫表面的焊渣和飛濺物，檢查焊縫外觀是否存在凹陷、凸起或咬邊等缺陷，若發現問題需進行補焊處理。對于暴露在室外環境中的鐵藝護欄，焊接點還需進行防腐處理，可采用涂刷防銹漆或鍍鋅的方式，防止焊接點因銹蝕而逐漸弱化。同時，必要時可對焊接點進行敲擊處理，消除焊接應力，避免后期使用過程中因應力釋放導致焊縫開裂。

　　The treatment after welding also affects the firmness and durability of the welding point. After welding is completed, it is necessary to promptly clean the welding slag and spatter on the surface of the weld, check the appearance of the weld for defects such as dents, protrusions, or undercuts, and if any problems are found, repair welding treatment should be carried out. For iron guardrails exposed to outdoor environments, anti-corrosion treatment is also required for welding points, which can be achieved by applying anti rust paint or galvanizing to prevent the welding points from gradually weakening due to corrosion. At the same time, if necessary, tapping treatment can be carried out on the welding points to eliminate welding stress and avoid weld cracking caused by stress release during later use.

　　保障鐵藝護欄焊接點的牢固性，本質上是通過嚴謹的前期準備、規范的焊接操作和細致的后期處理，確保焊接點能有效傳遞荷載、抵抗外力作用，從而讓鐵藝護欄在長期使用中保持結構穩定，發揮應有的防護作用。

　　Ensuring the firmness of the welding points of wrought iron guardrails essentially involves rigorous preliminary preparation, standardized welding operations, and meticulous post-processing to ensure that the welding points can effectively transmit loads and resist external forces, thereby maintaining structural stability and providing the necessary protection for wrought iron guardrails during long-term use.